Ferroborron Melting Kinetics in Thermite Mixture

Ferroborron Melting Kinetics in Thermite Mixture
Authors : Olexiy A. Tchaykovsky
Publication Date: 01-02-2016


Author(s):  Olexiy A. Tchaykovsky

Published in:   International Journal of Engineering Research & Technology

License:  This work is licensed under a Creative Commons Attribution 4.0 International License.

Website: www.ijert.org

Volume/Issue:   Volume. 5 - Issue. 02 , February - 2016

e-ISSN:   2278-0181


Cast parts with differentiated features significantly reduce operating costs but their production connected always with difficulties. Direct use the in-mold process for alloying cast iron with high temperature ferroalloys is not possible because their low dissolution. Dissolution process can be intensifying with thermites mixture. The thermite burning time as a function of ferroboron fraction and ferroboron insertion diameters were investigate. Ferroboron fractions were in a range 1..5 mm. Ferroboron cylindrical insertions diameter were 10, 15, 20 mm. The conditions and characteristics of ferroboron-thermite system, which is achieved complete melting of ferroboron were investigated.


Number of Citations for this article:  Data not Available


Key Word(s):    


Number of Downloads:     117

Call for Papers - May - 2017



                 Call for Thesis - 2017 

     Publish your Ph.D/Master's Thesis Online

              Publish Ph.D Master Thesis Online as Book