- Authors : Athira A R, Anu A
- Paper ID : IJERTCONV3IS29051
- Volume & Issue : NCRACE – 2015 (Volume 3 – Issue 29)
- Published (First Online): 30-07-2018
- ISSN (Online) : 2278-0181
- Publisher Name : IJERT
- License:
This work is licensed under a Creative Commons Attribution 4.0 International License
Experimental Study on Concrete by Partial Replacement of Cement with Phosphogypsum and Fine Aggregate with Thermosetting Plastics
Athira A R
Dept. of Civil Engineering YCET
Kollam, India
Anu A Assistant Professor
Dept. of Civil Engineering YCET
Kollam, India
Abstract – Concrete is a composite material composed mainly of water, aggregate, and cement. Usually there are additives and reinforcements included to achieve the desired physical properties of the finished material. For solving the disposal of large amount of recycled plastic material, reuse of plastic in concrete industry is considered as the most feasible application. The reuse of material can reduce the normal usage of ingredients in concrete and thereby reduce the cost of construction.
This study is focused on the use of thermo setting plastics as a partial replacement of aggregates in concrete. The aim was to investigate the characteristics of concrete with the addition of plastic and comparing it with the control mix, thereby determining the advantages and disadvantages of doing so. In this phosphogypsum is added to a 10% by partial replacement of cement. It is proposed to replace the aggregates partially with thermosetting plastics on the basis of percentage by weight such as 0%, 0.5%, 1%, 1.5%, 2% and 2.5%. The fresh concrete is tested for slump test and the compaction factor test, while the hardened concrete for compressive, tensile, flexural strength and durability.
Keywords Phosphogypsum, Thermosetting plastics, Durability
-
INTRODUCTION
Concrete is the most preferred and the single largest building material used by the construction industry. Concrete is a composite material composed mainly of water, aggregate, and cement. Usually there are additives and reinforcements included to achieve the desired physical properties of the finished material. When these ingredients are mixed together, they form a fluid mass that is easily molded into shape. Over time, the cement forms a hard matrix which binds the rest of the ingredients together into a durable stone-like material with many uses.
Research concerning the use of byproducts to augment the properties of concrete has been going on for many years. In the recent decades, the efforts have been made to use industry byproducts such as fly ash, silica fume, ground granulated blast furnace slag (GGBS), glass cullet, etc., in civil constructions. The potential applications of industry byproducts in concrete are as partial aggregate replacement or
as partial cement replacement, depending on their chemical composition and grain size. The use of these materials in concrete comes from the environmental constraints in the safe disposal of these products. Big attention is being focused on the environment and safeguarding of natural resources and recycling of wastes materials. Actually many industries are producing a significant number of products which incorporate scrap (residues). In the last 20 years, a lot of works concerning the use of several kinds of urban wastes in building materials industrials process have been published. Many research have been extended to study new kinds of wastes to investigate deeply particular aspects. The addition of wastes, a part from the environmental benefits, also produces good effects on the properties of final products.
One of the new waste materials used in the concrete industry is recycled plastic. For solving the disposal of large amount of recycled plastic material, reuse of plastic in concrete industry is considered as the most feasible application.
Phosphogypsum is a by-product of phosphate fertilizer plants and chemical industries. As it is contaminated with the impurities that impair the strength development of calcined products, it can be used as partial replacement of cement. above 10% replacement of phosphogypsum in concrete lead to drastic reduction not only in the compressive strength but in the split-tensile strength also; the flexural strength decreases as width and number of cracks increases significantly at replacement above 10% of cement with phosphogypsum at different water binder ratios.
The word plastic means substances which have plasticity, and accordingly, anything that is formed in a soft state and used in a solid state can be called a plastic. Therefore, the origin of plastic forming can be traced back to the processing methods of natural high polymers such as lacquer, shellac, amber, horns, tusks, tortoiseshell, as well as inorganic substances such as clay, glass, and metals. Because the natural high polymer materials are not uniform in quality and lack mass productivity in many cases, from early times it has been demanded in particular to process them easily and into better quality and to substitute artificial materials for
natural high polymers. Celluloid, synthetic rubber, ebonite, and rayon are these artificial materials. Presently, it is defined that the plastics are synthesized high polymers which have plasticity, and consequently substances made of these natural materials are precluded.
In India, about 6 million tons of waste gypsum such as phosphogypsum, flourogypsum etc., are being generated annually. Phosphogypsum is a by-product in the wet process for manufacture of phosphoric acid (ammonium phosphate fertilizer) by the action of sulphuric acid on the rock phosphate. It is produced by various processes such as dihydrate,hemi hydrate or anhydrite processes. In India the majority of phosphogypsum is produced by the dehydrate process due to its simplicity in operation and lower maintenance as compared to other processes. The other sources of phosphogypsum are by-products of hydrofluoric acid and boric acid industries
The objectives of the present study are:
-
To study the workability of fresh concrete.
-
To study the mechanical properties of concrete in hardened state.
-
To study the durability of concrete
-
-
EXPERIMENTAL INVESTIGATION
The aim of the experimental investigation is to ascertain and compare the improvement in the performance of concrete by the partial replacement of fine aggregate with thermosetting plastics and cement with a constant percentage of phosphogypsum thereby to arrive at the optimum replacement percentage of thermosetting plastic and to study durability of concrete mix. This study provides a comprehensive overview of engineering and construction properties of thermosetting plastics and phosphogypsum for use in concrete as partial replacement materials.
-
Test on constituent materials
Cement: Ordinary Portland cement of 53 grade conforming to IS 12269:1987 was used for the study. For the cement the standard consistency test, initial setting time test, final setting time test, specific gravity test and mortar cube compressive strength were conducted. Laboratory tests are conducted on cement to determine its standard consistency, initial setting time, final setting time and compressive strength. The standard consistency of the cement used is 36.25%
Phosphogypsum: Phosphogypsum is a by-product in the wet process for manufacture of phosphoric acid (ammonium phosphate fertilizer) by the action of sulphuric acid on the rock phosphate. The other sources of phosphogypsum are by- products of hydrofluoric acid and boric acid industries.
Current worldwide production of phosphoric acid yields over 100 million tons of phosphogypsum per year. While most of the rest of the world looked at phosphogypsum as a
valuable raw material and developed process to utilize it in chemical manufacture and building prodcts, India blessed with abundant low-cost natural gypsum piled the phosphogypsum up rather than bear the additional expense of utilizing it as a raw material.
It should be noted that during most of this time period the primary reason phosphogypsum was not used for construction products in India was because it contained small quantities of silica, fluorine and phosphate as impurities and fuel was required to dry it before it could be processed for some applications as a substitute for natural gypsum, which is a material of higher purity. However, these impurities impair the strength development of calcined products. It has only been in recent years that the question of radioactivity has been raised and this question now influences every decision relative to potential use in building products in this country.
Phosphogypsum used in the work is shown in Fig.1.
Specific gravity of phosphogypsum is 3.2
Fig. 1 Phosphogypsum
Fine aggregate: Commercially available M sand with 4.75 mm maximum size was used as fine aggregate. All physical properties were tested as per IS 383:1970. Specific gravity and fineness modulus of M-Sand used were 2.36 and 2.67 respectively.
Thermosetting plastic cannot be melted by heating because the molecular chains are bonded firmly with meshed crosslink. These plastic types are known as phenolic, melamine, unsaturated polyester, epoxy resin, silicone, and polyurethane. At present, these plastic wastes are disposed by either burning or burying. However, these processes are costly. If the thermosetting plastic waste can be reused, the pollution that is caused by the burning process as well as the cost of these waste management processes can be reduced. To achieve this purpose, a study of these thermosetting plastics for application into construction materials has been conducted, particularly for the concrete wall in buildings.
Thermosetting plastics are collected in the form of recycled plastics (RP). The plastic is green in color and it poses a size of 2.36 mm. Thermosetting plastics used in this work is shown in Fig.2. Physical properties such as specific gravity and fineness modulus of steel slag used were 2and 2.7 respectively.
Fig. 2 Thermosetting plastics
Coarse aggregate: Coarse aggregate used in this study were 20mm nominal size. The properties of coarse aggregate conforming to the IS 383:1970. The coarse aggregate used was found to belong to standard zone. Specific gravity and fineness modulus of coarse aggregate used were 2.65 and 6.49 respectively.
Water: Potable water is generally considered as being acceptable. Hence water available in the college water supply system was used for casting as well as curing of the test specimens.
-
Mix design
M25 mix was designed as per IS10262:2009 and the mix proportion was obtained as 1: 1.262 : 2.313. Water-cement ratio was 0.4. Six mixes were made namely RP0, RP0.5,RP1, RP1.5, RP2 and RP2.5 to determine mechanical properties. RP0 with 0% thermosetting plastic is considered as control mix. Other mixes are obtained by partial replacement of fine aggregate by 0.5%,1%,1.5%,2% and 2 .5% . In these mixes cement is partially replaced with 10% phophogypsum..Mix designation and Quantities of ingredients used for mix proportions are given in Table 1 and Table 2.
Sl.No
Mixes
Fine aggregate
Binding material
Thermos etting plastics weight (%)
M
sand (%)
Phospho- gypsum (%)
Cement (%)
1
RP0
0
100
0
100
2
RP1
0.5
99.5
10
90
3
RP2
1
99
10
90
4
RP3
1.5
98.5
10
90
5
RP4
2
98
10
90
6
RP5
2.5
97.5
10
90
Sl.No
Mixes
Fine aggregate
Binding material
Thermos etting plastics weight (%)
M
sand (%)
Phospho- gypsum (%)
Cement (%)
1
RP0
0
100
0
100
2
RP1
0.5
99.5
10
90
3
RP2
1
99
10
90
4
RP3
1.5
98.5
10
90
5
RP4
2
98
10
90
6
RP5
2.5
97.5
10
90
TABLE 1 MIX DESIGNATION FOR DIFFERENT MIXES
TABLE 2 QUANTITIES OF INGREDIENTS USED FOR MIX PROPORTIONS
Particulars
Quantity ( kg/m3 )
Cement
314.53
Fine aggregate
396.937
Coarse aggregate
727.414
Water
125.812
-
Specimen details
The specimens are standard cubes of 150mm side and 100mm side, cylinders of diameter 150mm and 300mm height, beams of size 500x100x100mm. Details of number of specimens are given in Table 3.
TABLE 3 SPECIMEN DETAILS
Sl. No
Specimen
Property
Size
Numbers
1
Cube
Compressiv e strength
150150150m
m
54
2
Cylinder
Split tensile strength
300mm height and 150mm diameter
18
3
Beam
Flexural strength
500100100m
m
18
4
Small cube
Durability
100100100m
m
72
Total number of specimens
162
-
Preparation and casting of specimens
For each mix nine concrete cubes of size 150x150x150mm for compressive strength test, three cylinders of 150mm diameter and 300mm height for compressive and splitting tensile strength test and twelve cubes of size 100x100x100 mm for durability test were casted.
-
Tests on specimens
Testing of concrete specimens plays an important role in controlling and confirming the quality of concrete. All the specimens cast were subjected to testing in order to study the effect of partial replacement of cement with constant amount of phosphogypsum and fine aggregate with thermosetting plastics on workability, strength and durability. Thus the experimental investigation carried out was divided in to three main headings. They are as follows:
-
Study on workability
-
Slump test
-
Compacting factor test
-
-
Study on strength
-
Compressive strength test
-
Splitting tensile strength test
-
Flexural strength test
-
-
Study on durability
-
-
-
RESULTS AND DISCUSSION
-
roperties of fresh concrete
Studies conducted on fresh properties are given in Table
-
From the results obtained it can be concluded that the slump and compacting factor increases with the percentage increase in replacement of fine aggregate with thermosetting plastics. Except RP0 cement is partially replaced with a constant amount of phosphogypsum.
TABLE 4 PROPERTIES OF FRESH CONCRETE
Sl.No.
Mix designation
Workability
Slump (mm)
Compacting factor
1
RP0
27
0.80
2
RP1
29
0.83
3
RP2
31
0.86
4
RP3
34
0.89
5
RP4
36
0.90
6
RP5
38
0.94
-
-
Properties of hardened concrete
Cube Compressive Strength: Compressive strength of all concrete mix was determined at 3, 7 and 28 days of curing. Comparing with the control mix the compressive strength gradually increased up to 2% and then decreased. From this study 2% of replacement of fine aggregate with thermosetting plastics and a constant amount of 10% replacement of cement with phosphogypsum was taken as the optimum mix. The increase in strength of RP4 is 6.86N/mm2.Compared to the normal mix RP4 shows a better strength value.
Splitting Tensile Strength: Splitting tensile strength of cylinder was maximum for 2% replacement of fine aggregate with thermosetting plastics and a constant amount of 10% replacement of cement with phosphogypsum. The increase in strength of RP4 is 6.86N/mm2.Compared to the normal mix RP4 shows a better strength value.
Flexural Strength of Beams: Flexural strength of beam was maximum for 2% of replacement of fine aggregate with thermosetting plastics and a constant amount of 10% replacement of cement with phosphogypsum. The increase in strength of RP4 is 13.4N/mm2. The strength of RP0 is 6.6 N/mm2 which is smaller as compared to RP4 value.
-
Durability of concrete
The durability of concrete is the ability to resist weathering action, chemical attack, abrasion, or any process of deterioration. Durable concrete will retain its original form, quality, and serviceability when exposed to its environment. For the study of durability of concrete the test conducted were Acid resistance test (Sulphuric Acid attack), Alkalinity test (Sodium hydroxide attack), Sulphate attack test, Seawater attack test.
-
Sulphuric Acid Attack Test – The weight and compressive strength of specimens immersed in H2SO4
solution at 56 and 90 days were determined and compared with normal cured specimen at 28 days. Fig 3 and Fig 4 shows the percentage strength loss and percentage weight loss respectivelly
80
60
40
20
0
56 day
90 day
80
60
40
20
0
56 day
90 day
RP0 RP4 RP5
Mix Designation
RP0 RP4 RP5
Mix Designation
Percentage strength loss
Percentage strength loss
Percentage weight loss (%)
Percentage weight loss (%)
Fig 3 Percentage strength loss in acid solution
8
6
4
2
0
56 day
90 day
8
6
4
2
0
56 day
90 day
RP0 RP4 RP5
Mix Designation
RP0 RP4 RP5
Mix Designation
Fig 4 Percentage weight loss in acid solution
Thermosetting plastic concrete with phosphogypsum has less durability property in acid. The reduction in compressive strength increased with the increase in thermosetting plastic content after the exposure to sulphuric acid solution. Likewise the percentage weight loss was also higher for thermosetting plastic concrete than for control mix. This indicates that plastic concrete shows poor resistance to acid attack than control mix.
Percentage strength loss (%)
Percentage strength loss (%)
-
Sodium Hydroxide Attack – The specimens were tested and weighed after 56 and 90 days of NaOH exposure. Percentage strength loss and weight loss in alkaline solution is given in Fig 5 and Fig 6.
70
60
50
40
30
20
10
0
56 day
90 day
70
60
50
40
30
20
10
0
56 day
90 day
RP0 RP4 RP5
Mix Designation
RP0 RP4 RP5
Mix Designation
Fig 5 Percentage strength loss in alkaline solution
6
5
4
3
2
1
0
56 day
90 day
6
5
4
3
2
1
0
56 day
90 day
RP0 RP4 RP5
Mix Designation
RP0 RP4 RP5
Mix Designation
Percentage weight loss (%)
Percentage weight loss (%)
Fig 6 percentage weight loss in alkaline solution
Percentage strength loss (%)
Percentage strength loss (%)
-
Sulphate attack – To study the sulphate attack on concrete, the cubes were tested after 56 and 90 days of exposure to sulphate solution. The effect of sulphate attack on concrete specimen was assessed by measuring the compressive strength and weight loss at the respective test ages and compared them with water cured specimen at 28 day. Percentage strength loss and weight loss in sulphate solution is given in Fig 7 and Fig 8.
30
25
20
15
10
5
56 day
90 day
30
25
20
15
10
5
56 day
90 day
RP0
RP4
RP5
RP0
RP4
RP5
Mix Designation
Mix Designation
0
0
Percentage weight loss (%)
Percentage weight loss (%)
Fig 7 Percentage strength loss in sulphate solution
6
5
4
3
2
1
0
56 day
90 day
6
5
4
3
2
1
0
56 day
90 day
RP0 RP4 RP5
Mix Designation
RP0 RP4 RP5
Mix Designation
Fig 8 Percentage weight loss in sulphate solution
Thermosetting plastic concrete which contains phosphogypsum reduces the sulphate attack as compared with control mix. On 90th day the percentage strength loss for RP4 is about 8.63%. When compared to acid and alkali
attack, thermosetting plastic concrete shows better durability properties. This may be due to the presence of plastic and phosphogypsum in concrete mix. Replacing a portion of Portland cement with phosphogypsum reduces the amount of reactive aluminates (tricalcium aluminate) available for sulphate reaction
Percentage strength loss (%)
Percentage strength loss (%)
-
Sea water attack – To determine the effect of sea water on concrete, the cubes were tested after 56 and 90 days of exposure to sea water. The compressive strength and weight loss at the respective test ages were determined and compared them with water cured specimen at 28 day. Percentage strength loss and weight loss in sea water is given in Fig 9 and Fig 10.
-
70
60
50
40
30
20
10
0
56 day
90 day
70
60
50
40
30
20
10
0
56 day
90 day
RP0 RP4 RP5
Mix Designation
RP0 RP4 RP5
Mix Designation
Percentage weight loss (%)
Percentage weight loss (%)
Fig 9 Percentage strength loss in sea water
5
4
3
2
1
56 day
90 day
5
4
3
2
1
56 day
90 day
Mix Designation
Mix Designation
0
0
RP0
RP0
RP4
RP4
RP5
RP5
Fig 10 Percentage weight loss in sea water
Phosphogypsum present in the concrete decreases the durability in sea water. The compressive strength of concrete decreases with increase in days. The percentage loss in strength at 90 days for the mix RP0 was 56.7 % and for RP4 was 58.88 %. This indicates that RP0 showed better durability property than RP4. The weight loss obtained for RP0 was 3.4% and for RP4 was 3.85%. From this result it is clear that thermosetting concrete with phosphogypsum shows low resistant in sea water.
-
-
CONCLUSION
The major conclusions of my thesis work are presented below:
-
Workability increased with increase in thermosetting plastic content and provision of phosphogypsum by replacing with 10% of cement. Maximum workability was obtained at 2.5% of replacement of fine aggregate with thermosetting plastic and a partial replacement of 10% constant amount of cement with phosphogypsum.
-
Compressive strength increased upto 2% replacement of fine aggregate with thermosetting plastics and a replacement of 10% constant amount of cement with phosphogypsum. The strength value decreased at RP5. The increase in compressive strength at 28th day of RP4 was about 26.27% than control mix (RP0).
-
The splitting tensile strength of cylinder was maximum for 2% of replacement (RP4). The percentage of increase in splitting tensile strength of RP4 was about 34.77% than RP0.
-
The flexural strength of beam was maximum for RP4. The increase in strength of RP4 shows a considerable increment than RP0.
-
Thermosetting plastic concrete with phosphogypsum had less durability property in acid test. After 90 days exposure in sulphuric acid solution the compressive strength of RP4 was reduced by 63.45%. Percentage weight loss was much higher for RP4 as compared to RP0.
-
On curing in NaOH solution, the percentage strength loss for RP4 was about 57.74% at 90 days. The weight loss was also much higher for RP4 compared to RP0. So thermosetting plastic concrete with phosphogypsum was less durable compared to control mix.
-
The thermosetting plastic concrete with phosphogypsum reduced the sulphate attack as compared with control mix. On curing in sulphate solution , the percentage strength loss for RP4 was about 8.63% at 90 days. The weight loss was also much higher for RP4 compared to RP0.
-
Plastic concrete with phosphogypsum decreases the durability in sea water. The percentage loss in strength at 90 days for the mix RP0 was 56.7 % and for RP4 was
58.88 %. The weight loss obtained for RP0 was 3.4% and for RP4 was 3.85%.
The results presented in this thesis report indicate that the partial replacement of 10% portland cement with phosphogypsum and partial replacement of fine aggregate up to 2% with thermosetting plastics can obtain the maximum strength of concrete.
REFERENCES
-
Al-Manaseer. A.A and T.R. Dalal (1997) Concrete containing plastic aggregates, Concrete International, 4752.
-
Awan Alioune Ndiaye et al. (2005) Phosphogypsum based cement formulation in agreement with standard portland cement in the frame work of a concrete code policy for thermal and energetic efficiency of the building, 306-322.
-
Batayneh, M et al. (2006) Use of selected waste materials in concrete mixes, Waste Management ,27, 18701876
-
Bayasi, Z., Zeng, J (1993) Properties of polypropylene fiber reinforced concrete, ACI Materials Journal 90, 6 , 605610
-
Chang. W et al. (2010) Sulfate attack resistance of Portland cement mixtures containing phosphogypsum, Concrete durability, 2, 100 102.
-
Choi, Y.W et al.(2005) Effects of waste PET bottles aggregate on properties of concrete,Cement and Concrete Research, 35, 776781
-
Jo, B.W et al. (2007) Mechanical properties of polymer concrete made with recycled PET and recycled concrete aggregates, Construction and Building Materials.
-
Kalvakaalava. R et al (1996) Microstructural and Phase Characteristics of Phosphogypsum, 1118.
-
Khatib Z.K and Bayomy (1999) Rubberized portland cement concrete
ASCE Journal of Materials in Civil Engineering 11, 3, 206213.
-
Mahesh A. Bagade and Satone S.R (2012) Experimental investigation of partial replacement of cement by various percentage of phosphogypsum in cement concrete, 2, 785-787
-
Marzouk, O. Yet al. (2007) Valorization of post-consumer waste plastic in cementitious concrete composites, Waste Management,27,310318
-
Raghvan, D et al.(1998) Workability, mechanical properties and chemical stability of a recycled tire rubber-filled cementitious composite, Journal of Materials Science 33, 7, 17451752.